SPECIFICATION Supplier : Samsung electro-mechanics Samsung P/N : CL10B392KB8NFNC Product : Multi-layer Ceramic Capacitor Description : CAP, 3.9, 50V, 10%, X7R, 0603 A. Samsung Part Number Series Size CL 10 B 392 K B 8 N F N C Samsung Multi-layer Ceramic Capacitor 0603 (inch code) Dielectric X7R Capacitance 3.9 10 % Capacitance L: 1.6 0.1 mm 0.8 0.1 W: Inner electrode Ni Termination Cu Plating Sn 100% Product tolerance Rated Voltage 50 V Thickness 0.8 0.1 mm mm (Pb Free) Special Product for POWER application Reserved for future use Packaging Cardboard Type,7"reel(4,000ea) B. Samsung Reliability Test and Judgement condition Performance 1.00.2Vrms More than 500Mohm Rated Voltage 60~120 sec. Appearance No abnormal exterior appearance Withstanding No dielectric breakdown or Visual inspection 250% of the rated voltage Voltage mechanical breakdown Temperature X7R Characteristics Adhesive Strength (From -55 to 125, Capacitance change should be within 15%) No peeling shall be occur on the 500gF, for 101 sec. of Termination terminal electrode Bending Strength Capacitance change : Tan (DF) Insulation Within specified tolerance Test condition 110% Capacitance 0.025 max. Resistance within 12.5% Bending to the limit (1mm) with 1.0mm/sec. Solderability More than 75% of terminal surface SnAg3.0Cu0.5 solder is to be soldered newly 2455, 30.3sec. (preheating : 80~120 for 10~30sec.) Resistance to Capacitance change : Soldering heat Tan , IR : initial spec. within 7.5% Solder pot : 2705, 101sec. Performance Vibration Test Capacitance change : within 5% Tan , IR : initial spec. Moisture Capacitance change : Resistance Tan : 0.05 max IR Amplitude : 1.5mm From 10 to 55 (return : 1min.) 2hours 3 direction (x, y, z) within 12.5% With rated voltage 402, 90~95%RH, 500+12/-0 hours. : More than 25* High Temperature Capacitance change : Resistance Tan : 0.05 max IR Test condition within 12.5% With 200% of the rated voltage Max. operating temperature : More than 50* 1000+48/-0 hours. Temperature Capacitance change : Cycling Tan , IR : initial spec. within 7.5% 1 cycle condition Min. operating temperature 25 25 Max. operating temperature 5 cycles test C. Recommended Soldering method : Reflow ( Reflow Peak Temperature : 260+0/-5, 10sec. Max ) * For the more detail Specification, Please refer to the Samsung MLCC catalogue.