SPECIFICATION Supplier : Samsung electro-mechanics Samsung P/N : CL21C100JBANFNC Product : Multi-layer Ceramic Capacitor Description : CAP, 10, 50V, 5%, C0G, 0805 A. Samsung Part Number Series CL 21 C 100 J B A N F N C Samsung Multi-layer Ceramic Capacitor Size 0805 Dielectric C0G (inch code) L: 2.0 0.1 Capacitance tolerance 50 V Rated Voltage 0.65 0.1 Thickness mm W: 1.25 0.1 Inner electrode Ni Termination Cu Plating Sn 100% 10 5 % Capacitance mm mm (Pb Free) Product Product for POWER application Special Reserved for future use Packaging Cardboard Type, 7" reel B. Samsung Reliablility Test and Judgement condition Performance Within specified tolerance Test condition 110% 0.5~5Vrms Rated Voltage 60~120 sec. Resistance 10,000Mohm or 500Mohm Whichever is Smaller Appearance No abnormal exterior appearance Withstanding No dielectric breakdown or Microscope (10) 300% of the rated voltage Voltage mechanical breakdown Temperature C0G Characterisitcs Adhesive Strength (From -55 to 125, Capacitance change shoud be within 30PPM/) No peeling shall be occur on the 500gF, for 101 sec. of Termination terminal electrode Bending Strength Capacitance change : Bending to the limit (1mm) with 1.0mm/sec. Solderability within 5% or 0.5 whichever is larger More than 75% of terminal surface SnAg3.0Cu0.5 solder is to be soldered newly 2455, 30.3sec. Capacitance 600 min Q Insulation (preheating : 80~120 for 10~30sec.) Resistance to Capacitance change : Soldering heat within 2.5% or 0.25 whichever is larger Tan , IR : initial spec. Solder pot : 2705, 101sec. Performance Test condition Vibration Test Capacitance change : Moisture within 2.5% or 0.25 whichever is larger From 10 to 55 (return : 1min.) Tan , IR : initial spec. 2hours 3 direction (x, y, z) Capacitance change : With rated voltage Resistance within 7.5% or 0.75 whichever is larger 402, 90~95%RH, 500+12/-0hrs Q: 133.33 min IR : High Temperature Resistance Amplitude : 1.5mm 500Mohm or 25Mohm Whichever is Smaller Capacitance change : With 200% within 3% or 0.3 whichever is larger Q: 300 min Max. operating temperature IR : of the rated voltage 1000+48/-0hrs 1000Mohm or 50Mohm Whichever is Smaller Temperature Capacitance change : 1 cycle condition Cycling within 2.5% or 0.25 whichever is larger Min. operating temperature Tan , IR : initial spec. Max. operating temperature 5 cycle test C. Recommended Soldering method : Reflow ( Reflow Peak Temperature : 260+0/-5, 10sec. Max ) * For the more detail Specification, Please refer to the Samsung MLCC catalogue. 25 25